Appilications:
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects
Features:
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding
Technical data sheet:
How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.
2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.
3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.
4.At 25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.
Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects
Features:
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding
Technical data sheet:
| Model | 902-40 | 902-30 | H8225 | H8230 |
| Mixing ratio (A:B) | 100:2~3 | 100:2~3 | 1:1 | 1:1 |
| Hardness (Shore A)≥ | 25 | 30 | 25 | 30 |
| Tear-strength (kgf/c m²)≥ | 21 | 22 | 25 | 26 |
| Viscosity ( mixed 25°C mpa.S) | 25000±2000 | 25000±2000 | 18000±2000 | 20000±2000 |
| Shrinkagerate (%)≤ | 0.2 | 0.2 | 0.1 | 0.1 |
| Elongation(%) | 450 | 400 | 450 | 400 |
How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.
2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.
3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.
4.At 25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.
Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.